Characterization of Cellulose from Olive Pomace Extracted by Different Methods
Author:
Affiliation:

(College of Food Science and Engineering,Northwest A&F University,Yangling 712100,Shaanxi)

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    以橄榄果渣为原料,采用碱液浸提法从橄榄果渣中提取纤维素(初始纤维素),用2 mol/L HCl和H2SO4溶液水解初始纤维素,得到橄榄渣微晶纤维素(MCC)。测定初始纤维素与微晶纤维素的持水力、持油力和膨胀力。通过差示扫描量热仪(DSC)、傅里叶红外光谱仪(FTIR)、X射线衍射仪(XRD)、场发射扫描电镜(SEM)和激光共聚焦扫描显微镜(CLSM)对纤维素的性质进行表征。结果表明,经H2SO4和HCl水解得到的H2SO4-MCC和HCl-MCC的微观结构呈短棒状,表面平整排列。其持水力和膨胀力高于初始纤维素。H2SO4-MCC的结晶度和晶粒尺寸分别为75.77%和5.35 nm,HCl-MCC的结晶度和晶粒尺寸分别为64.92%和4.96 nm。与初始纤维素相比,微晶纤维素的乳化性能变好。FTIR图谱表明酸水解使纤维素中的木质素及半纤维素降解。DSC结果表明酸水解后微晶纤维素中水的蒸发温度升高,热降解温度降低。

    Abstract:

    Olive pomace was used to prepare cellulose by alkaline solution extraction,then microcrystalline cellulose (MCC) was obtained by further hydrolysis of cellulose with 2 mol/L HCl and H2SO4.Water-holding capacity (WHC),oil-holding capacity (OHC) and swelling capacity were measured and analyzed.Differential scanning calorimeter (DSC),Fourier transform infrared spectra (FTIR),X-ray diffraction (XRD),scanning electron microscope (SEM) and confocal laser scanning microscope(CLSM) were used to evaluate the physicochemical properties of primary cellulose and MCC.The results showed that morphology changed from loose to ordered array with rod-shape after hydrolyzing with H2SO4 and HCl.Besides,WHC and swelling capacity were increased.The crystallinity and crystal size of H2SO4-MCC are 75.77% and 5.35 nm,and that of HCl-MCC are 64.92% and 4.96 nm,respectively.Compared with the primary cellulose,emulsification characteristics of MCCs were also improved.FTIR spectra proved the lignin and hemicellulose degraded after acid hydrolysis.DSC results showed MCC had higher water evaporation temperature but lower thermal degradation temperature.

    参考文献
    相似文献
    引证文献
引用本文

郭艳,王悦,张依,孟焕娜,李志西,冯宪超.不同方法提取的橄榄果渣纤维素的性质表征[J].中国食品学报,2022,22(1):306-313

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2021-01-12
  • 最后修改日期:
  • 录用日期:
  • 在线发布日期: 2022-02-11
  • 出版日期:
文章二维码
版权所有 :《中国食品学报》杂志社     京ICP备09084417号-4
地址 :北京市海淀区阜成路北三街8号9层      邮政编码 :100048
电话 :010-65223596 65265375      电子邮箱 :chinaspxb@vip.163.com
技术支持:北京勤云科技发展有限公司

漂浮通知